Doubling performance with lithium metal that doesn't catch fire

Researchers at the University of Michigan have developed a rechargeable battery technology that could double the output of today’s lithium ion cells, extending electric vehicle ranges and time between cell phone charges, without taking up any added space.

Using a ceramic, solid-state electrolyte, engineers have been able to harness the power of lithium metal batteries without the historic issues of poor durability and short-circuiting.

“This could be a game-changer – a paradigm shift in how a battery operates,” said Jeff Sakamoto, a U-M associate professor of mechanical engineering who leads the work.

Current lithium ion batteries max out with a total energy density around 600 watt-hours per litre(Wh/L) at the cell level. In principal, solid-state batteries can reach 1,200 Wh/L.

To solve lithium metal’s combustion problem, U-M engineers created a ceramic layer that stabilises the surface and keeps dendrites from forming and preventing fires. It allows batteries to harness the benefits of lithium metal i.e. energy density and high-conductivity, but without the dangers of fires or degradation over time.

“What we’ve come up with is a different approach – physically stabilising the lithium metal surface with a ceramic,” Sakamoto said. “It’s not combustible. And there’s no liquid, which is what typically fuels the battery fires you see. You get rid of that fuel, you get rid of the combustion.”

In earlier solid-state electrolyte tests, lithium metal grew through the ceramic electrolyte at low charging rates, causing a short circuit, much like that in liquid cells. U-M researchers solved this problem with chemical and mechanical treatments that provide a pristine surface for lithium to plate evenly, effectively suppressing the formation of dendrites or filaments. Not only does this improve safety, it enables a dramatic improvement in charging rates, Sakamoto said.

“Up until now, the rates at which you could plate lithium would mean you’d have to charge a lithium metal car battery over 20 to 50 hours (for full power),” Sakamoto said. “With this breakthrough, we demonstrated we can charge the battery in 3 hours or less.

“We’re talking a factor of 10 increase in charging speed compared to previous reports for solid state lithium metal batteries. We’re now on par with lithium ion cells in terms of charging rates, but with additional benefits. “

That charge/recharge process is what inevitably leads to the eventual death of a lithium ion battery. Repeatedly exchanging ions between the cathode and anode produces visible degradation right out of the box.

In testing the ceramic electrolyte, however, no visible degradation is observed after long term cycling, said Nathan Taylor, a U-M post-doctoral fellow in mechanical engineering.

“We did the same test for 22 days,” he said. “The battery was just the same at the start as it was at the end. We didn’t see any degradation. We aren’t aware of any other bulk solid-state electrolyte performing this well for this long.”

Bulk solid-state electrolytes enable cells that are a drop-in replacement for current lithium ion batteries and could leverage existing battery manufacturing technology. With the material performance verified, the research group has begun producing thin solid electrolyte layers required to meet solid state capacity targets.

Above: Nathan Taylor, a post-doctoral fellow in mechanical engineering, inspects a piece of lithium metal in the Phoenix Memorial Laboratory building at the University of Michigan.

Author
Neil Tyler

Let’s block ads! (Why?)

New Electronics News

Click to comment

Leave a Reply

Your email address will not be published. Required fields are marked *

To Top
Social Media Auto Publish Powered By : XYZScripts.com